中空玻璃的生產(chǎn)過程中非常重要的就是密封環(huán)節(jié)了，除此之外還有一個同樣重要而且在操作系數(shù)上來說也是更加困難。中空玻璃的賣點就在于隔音隔熱、保溫等一系列優(yōu)良性能，這些性能靠的基本就是中間的充氣、之后的密封，這兩步驟決定了中空玻璃質(zhì)量、性能的好壞。今天小編就給大家說說關于中空玻璃的生產(chǎn)條件與組裝要求。
In the production process of hollow glass, the sealing link is particularly important. In addition, there is an equally important and more difficult operation factor. The selling point of hollow glass lies in a series of excellent performances, such as sound insulation, heat insulation and so on. These performances depend on the gas filling in the middle and sealing afterwards. These two steps determine the quality and performance of hollow glass. Today, Xiaobian will tell you about the production conditions and assembly requirements of hollow glass.
中空玻璃的原理與充氣生產(chǎn)過程控制：
Principle of hollow glass and control of aeration process:
中空玻璃中間夾層是要充進惰性氣體，惰性氣體不容易與外界發(fā)生反應，所以這才能讓中空玻璃具備隔音、隔熱等優(yōu)良性能。在中空玻璃中的惰性氣體多用氬氣，但是氬氣是一種無色無味的氣體，且其充氣濃度不易測量。那如何測量，充氣中空玻璃呢。
Interlayer of hollow glass is filled with inert gas, which is not easy to react with the outside world, so it can make hollow glass have sound insulation, heat insulation and other excellent properties. Argon is often used as inert gas in hollow glass, but argon is a colorless odorless gas, and its aeration concentration is difficult to measure. So how to measure it? Inflatable hollow glass.
充氣中空玻璃的生產(chǎn)過程控制概念是，為確保充氣中空玻璃生產(chǎn)過程處于受控狀態(tài)，對影響充氣濃度質(zhì)量的生產(chǎn)過程所采取的作業(yè)技術和生產(chǎn)過程的分析、診斷和實時監(jiān)控。它的作用在于對生產(chǎn)過程的質(zhì)量控制進行系統(tǒng)安排，對直接或間接影響過程質(zhì)量的因素進行核心控制并制定實施控制計劃，確保過程質(zhì)量。
The concept of production process control of pneumatic hollow glass is to ensure that the production process of pneumatic hollow glass is in a controlled state, and to analyze, diagnose and real-time monitor the operation technology and production process that affect the quality of pneumatic concentration. Its function is to arrange the quality control of production process systematically, to control the factors that directly or indirectly affect the quality of production process, and to formulate and implement control plans to ensure the quality of production process.

中空玻璃充氣生產(chǎn)過程中需要注意的事項：
Attentions should be paid in the production of air-filled hollow glass:
充氣中空玻璃中的氬氣需要大約6~8小時才能完全擴散，因此，對中空玻璃氬氣初始濃度的檢測需在氣體完全擴散后才能進行。因此，無論是對充氣中空玻璃濃度的在線檢測抑或是在惰性氣體完全擴散的6~8小時后再檢測
It takes about 6 to 8 hours for argon to diffuse completely in air-filled hollow glass. Therefore, the initial concentration of argon in air-filled hollow glass can only be detected after the gas diffuses completely. Therefore, either on-line measurement of the concentration of the aerated hollow glass or after 6-8 hours of complete diffusion of the inert gas
造成充氣中空玻璃初始濃度低的主要原因在于充氣過程中出現(xiàn)的紊流現(xiàn)象。對充氣中空玻璃生產(chǎn)控制的意義在于對整個充氣過程進行實時監(jiān)控，從而有效地避免中空玻璃充氣過程中可能出現(xiàn)的紊流現(xiàn)象，提高和保證充氣質(zhì)量的穩(wěn)定性。
The main reason for the low initial concentration of aerated hollow glass is the turbulence phenomenon in the process of aeration. The significance of production control of aerated hollow glass lies in real-time monitoring of the whole aeration process, so as to effectively avoid turbulent phenomena that may occur during the aeration process of the hollow glass, and to improve and ensure the stability of the aeration quality.
中空玻璃的組裝要求：
Assembly requirements for hollow glass:
對環(huán)境的要求：溫度也應在10-30度之間；2、相對濕度的要求：此種中空玻璃對相對濕度的要求稍低一些，正常情況即可。但應注意的是，干燥劑應選擇正規(guī)廠家的合格產(chǎn)品，以保證干燥劑的有效使用。干燥劑開封后很好于二十四小時之內(nèi)用完，因為聚硫膠的透氣性較大，密封性差，因此要采用雙道密封。用丁基膠作為一道密封，起到陰隔氣體的作用。用聚硫膠作為第二道密封，主要作用是粘結作用，其次才是隔氣作用。實踐證明，單產(chǎn)密封的中空玻璃壽命只有5年左右，而雙道密封的中空玻璃壽命可長達20年甚至40年以上
Environmental requirements: temperature should also be between 10 - 30 degrees; 2. Relative humidity requirements: this kind of hollow glass relative humidity requirements are slightly lower, normal conditions can be. However, it should be noted that driers should select qualified products from regular manufacturers to ensure the effective use of driers. The desiccant is better to be used up within 24 hours after opening, because polysulfide rubber has a large air permeability and poor sealing, so double-channel sealing should be adopted. Butyl rubber is used as a seal to isolate gas. Using polysulfide glue as the second seal, the main function is bonding, followed by gas insulation. Practice has proved that the service life of single-product sealed hollow glass is only about 5 years, while that of double-channel sealed hollow glass can be as long as 20 years or even more.